GRADE COMPARISON
CYCOLAC™ Resin MG47F | CYCOLAC™ Resin MG94F | |||
---|---|---|---|---|
Region | Europe | Europe | ||
MECHANICAL | ||||
Tensile Modulus, 1 mm/min (ISO 527) | 2370 MPa | 2400 MPa | ||
Tensile Stress, yield, 50 mm/min (ISO 527) | 47 MPa | 45 MPa | ||
Flexural Modulus, 2 mm/min (ISO 178) | 2200 MPa | 2450 MPa | ||
Tensile Stress, break, 50 mm/min (ISO 527) | 35 MPa | 35 MPa | ||
Tensile Strain, break, 50 mm/min (ISO 527) | 25 % | 45 % | ||
Tensile Strain, yield, 50 mm/min (ISO 527) | 2.6 % | 2.2 % | ||
Flexural Stress, yield, 2 mm/min (ISO 178) | 70 MPa | 65 MPa | ||
IMPACT | ||||
Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm (ISO 179/1eA) | 9 kJ/m² | 10 kJ/m² | ||
Izod Impact, notched 80*10*4 +23°C (ISO 180/1A) | 22 kJ/m² | 18 kJ/m² | ||
Izod Impact, notched 80*10*4 -30°C (ISO 180/1A) | 8 kJ/m² | 7 kJ/m² | ||
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm (ISO 179/1eA) | 26 kJ/m² | 23 kJ/m² | ||
THERMAL | ||||
Vicat Softening Temp, Rate B/120 (ISO 306) | 100 °C | 100 °C | ||
Vicat Softening Temp, Rate B/50 (ISO 306) | 98 °C | 99 °C | ||
PHYSICAL | ||||
Density (ISO 1183) | 1.04 g/cm³ | 1.04 g/cm³ | ||
Melt Flow Rate, 230°C/3.8 kg (ASTM D1238) | 5.6 g/10 min | 11.7 g/10 min | ||
FLAME CHARACTERISTICS | ||||
UL Yellow Card Link (-) | E45329-102071279 | E45329-102071280 | ||
INJECTION MOLDING | ||||
Mold Temperature | 50-70 °C | 40-80 °C | ||
Nozzle Temperature | 220-260 °C | 210-250 °C | ||
Maximum Moisture Content | 0.1 % | 0.1 % | ||
Melt Temperature | 220-260 °C | 220-260 °C | ||
Middle - Zone 2 Temperature | 205-225 °C | 220-260 °C | ||
Drying Time | 2-4 Hrs | 2-4 Hrs | ||
Front - Zone 3 Temperature | 215-240 °C | 220-260 °C | ||
Drying Temperature | 80-95 °C | 85-95 °C | ||
Rear - Zone 1 Temperature | 190-210 °C | 200-240 °C |